duplex stainless steel; welding; annealing; microstructure; impact toughness; tensile tests
The phase transformations and mechanical behaviour during welding and subsequent annealing treatment of 2205 duplex stainless steel have been investigated. Detailed microstructural examination showed the presence of higher ferrite amounts in the heat affected zone (HAZ), while higher amounts of austenite were recorded in the centre region of the weld metal. Annealing treatments in the temperature range of 800-1000 degrees C resulted in a precipitation of sigma phase and M23C6 chromium carbides at the gamma/delta interfaces that were found to be preferential precipitation sites. Above 1050 degrees C, the volume fraction of delta ferrite increases with annealing temperature. The increase of delta ferrite occurs at a faster rate in the HAZ than in the base metal and fusion zone. Optimal mechanical properties and an acceptable ferrite/ austenite ratio throughout the weld regions corresponds to annealing at 1050 degrees C. Fractographic examinations showed that the mode of failure changed from quasi-cleavage fracture to dimple rupture with an increase in the annealing temperature from 850 to 1050 degrees C. (c) 2007 Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据