MATERIALS & DESIGN
卷 57, 期 -, 页码 487-493出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2013.12.051
关键词
Magnesium alloy; Metadynamic recrystallization; Double-hit hot compression test
Metadynamic recrystallization (MDRX) behavior of AZ61 magnesium alloy and its effects on flow behavior and microstructure evolution have been investigated in this study. Towards this end, a set of double-hit hot compression tests was conducted under strain rate of 0.1 s (1) at 400 degrees C. To differentiate the static and metadynamic recrystallization dominant strain regions, the first stage of deformation was carried out up to the different pre-strains with a constant inter-pass annealing time of 200 s. The results indicated that the MDRX is predominant recrystallization mechanism where the pre-strains are higher than 0.35. Furthermore, to investigate the influence of MDRX on subsequent flow behavior and the related microstructure, an elaborated inter-pass annealing treatment was executed employing a range of inter-pass annealing time (2-500 s). The results show that the progress of MDRX leads to an increase in the flow stress as well as the rate of work hardening encountered in the subsequent deformation. Additionally, the microstructural examinations confirm that the observed hardening phenomenon is a consequence of grain growth evolved from MDRX and its direct effect on the onset of dynamic recrystallization at the second stage of deformation. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据