MATERIALS & DESIGN
卷 47, 期 -, 页码 522-528出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2012.12.033
关键词
Aluminium alloys; Grain refinement; Mechanical property
资金
- National Natural Science Foundation of China [51071097, 51271101]
- National Basic Research Program of China [2012CB825702]
A new Al-3Ti-1B-0.2C master alloy with uniform microstructure was prepared using a melt reaction method in this study. In the master alloy, TiB2 particles exhibit hierarchical dendritic morphology, while TiC particles doped with a trace amount of B show a polyhedral morphology. The grain refining performance of the master alloy on A356 alloy has also been investigated. It is found that the addition of 0.2 wt.% Al-3Ti-1B-0.2C master alloy can induce very effective grain refinement of the A356 alloy. The average grain size of alpha-Al is reduced to 167 +/- 8 mu m from about 1570 mu m and the grain refining efficiency does not fade obviously within 60 min. Therefore, the mechanical properties of the A356 alloy have been improved obviously by the addition of the Al-3Ti-1B-0.2C master alloy, including the ultimate tensile strength, yield strength and elongation. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据