Fully dense Zirconium Diboride (ZrB2)-based ceramics with Zirconium Silicide (ZrSi2) and Silicon Carbide platelet (SiCpl) additive were fabricated by hot-press sintering in flowing argon atmosphere. Their mechanical properties and microstructure were examined. The contents of ZrSi2 and SiCpl were optimized. The defined addition of ZrSi2 was beneficial for densification and improving the mechanical properties of the ZrB2-based ceramics. The addition of SiCpl obviously improved the fracture toughness of the ZrB2-based ceramics. The range of fracture toughness of ZrB2-SiCpl-ZrSi2 composite was 6.7-9.0 MPa m(1/2). The flexural strength of the composites varied a little and the maximum was 597 MPa when the content of ZrSi2 and Sic(pl) was both 5 vol.%. XRD results showed that a small amount of Zirconium Carbide (ZrC) formed during sintering. The microstructure of the composites was fine, compact and homogeneous. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据