MATERIALS & DESIGN
卷 33, 期 -, 页码 340-344出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2011.07.056
关键词
-
资金
- CNPq
- Finep
- Petrobras
This investigation focuses on the analysis of fracture toughness characteristics of Friction Hydro-Pillar Process (FHPP) welded joints in C-Mn steels. Crack tip opening displacement (CTOD) tests were performed to analyze the influence of axial loads applied during welding on fracture toughness. For this evaluation compact tension C(T) specimens were used with notches located at the bonding line of the welded specimens. The welding process produced a significant reduction of toughness independent of the axial force applied. Fractographic analysis indicated that the fracture process occurred by microvoid coalescence. The variation in the morphology of the prior inclusions resulting from welding was responsible for the observed decrease in toughness. (C) 2011 Elsevier Ltd. All rights reserved.