期刊
MATERIALS & DESIGN
卷 40, 期 -, 页码 117-123出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2012.03.041
关键词
Welding; Mechanical; Microstructure
资金
- National High Technology Research and Development Program of China (National 863 plans projects) [2009AA03Z516]
Al-4.7Mg-0.7Mn-0.3Er alloy plates were welded by laser beam welding (LBW) and tungsten inert gas (TIG). Mechanical properties and microstructures of both welded joints were analyzed. The results showed that the tensile strength of LBW joint was 315 MPa, which was approximately 10% higher than that of TIG welded joint. This was attributed to the fine grains, dispersed primary Al3Er phase and low Mg evaporation in LBW weld. Equiaxed grains with average size of 30 mu m were obtained in the fusion zone, which were much smaller than that of 90 mu m in the fusion zone of TIG joint, due to the low heat input during LBW process. Moreover, finer primary Al3Er particles were uniformly distributed in the LBW joints, which resulted in a substantial increase of nucleation rate in LBW welds. In addition, it was also found that Mg concentrations in the fusion zones, in both TIG and LBW joints, were lower than that of the base one tested by EPMA. The burning loss rates of Mg in TIG and LBW joints were 36% and 22%, respectively. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据