关键词
Microstructure; Mechanical properties; Dissimilar materials joints
资金
- National Natural Science Foundation of China [50871076]
- Shanghai Leading Academic Discipline Project [B113]
In this paper, 192 martensitic steel and S304H austenitic steel were welded by gas tungsten arc welding (GTAW) process. Microstructural features and mechanical properties of T92 and S304H dissimilar materials joints were investigated. The results showed that the part of the joints with relatively weak tensile strength was T92 coarse-grained heat affected zone (CGHAZ), while the part of the joints which revealed relatively weak toughness was weld metal. The decrease of tensile strength in T92 CGHAZ was due to its coarse tempered martensite structure. Weak toughness of the joints was resulted from the coarse dendritic austenite of the weld metal. However, the weld metal in transverse direction of the joints was provided higher tensile strength by the orientation distribution of grains compared with 192 CGHAZ. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据