期刊
APPLIED SURFACE SCIENCE
卷 349, 期 -, 页码 970-982出版社
ELSEVIER
DOI: 10.1016/j.apsusc.2015.04.106
关键词
Transparent conducting oxide; Band bending; Dopant solubility; Ceramic
类别
资金
- SFI through the PI program [06/IN.I/I92]
- EPSRC funded Centre for Innovation [EP/K000144/1, EP/K000136/1]
- EPSRC [EP/L000202, EP/K014099/1, EP/F019823/1]
- Royal Society [UF100105]
- Marie Curie Intra European Fellowship within the 7th European Community Framework Programme the European Union [PIEF-GA-2010-274999]
- Trinity College Oxford
- EPSRC [EP/H006060/1, EP/K000144/1, EP/K014099/1, EP/F019823/1, EP/L000202/1, EP/K000136/1] Funding Source: UKRI
- Engineering and Physical Sciences Research Council [EP/K000144/1, EP/K000136/1, EP/K014099/1, EP/H006060/1, EP/F019823/1, EP/L000202/1] Funding Source: researchfish
The limit of solubility of Ga2O3 in the cubic bixbyite In2O3 phase was established by X-ray diffraction and Raman spectroscopy to correspond to replacement of around 6% of In cations by Ga for samples prepared at 1250 degrees C. Density functional theory calculations suggest that Ga substitution should lead to widening of the bulk bandgap, as expected from the much larger gap of Ga2O3 as compared to In2O3. However both diffuse reflectance spectroscopy and valence band X-ray photoemission reveal an apparent narrowing of the gap with Ga doping. It is tentatively concluded that this anomaly arises from introduction of Ga+ surface lone pair states at the top of the valence band and structure at the top of the valence band in Ga-segregated samples is assigned to these lone pair states. In addition photoemission reveals a broadening of the valence band edge. Core X-ray photoemission spectra and low energy ion scattering spectroscopy both reveal pronounced segregation of Ga to the ceramic surface, which may be linked to both relief of strain in the bulk and the preferential occupation of surface sites by lone pair cations. Surprisingly Ga segregation is not accompanied by the development of chemically shifted structure in Ga 2p core XPS associated with Ga+. However experiments on ion bombarded Ga2O3, where a shoulder at the top edge of the valence band spectra provide a clear signature of Ga+ at the surface, show that the chemical shift between Ga+ and Ga3+ is too small to be resolved in Ga 2p core level spectra. Thus the failure to observe chemically shifted structure associated with Ga+ is not inconsistent with the proposal that band gap narrowing is associated with lone pair states at surfaces and interfaces. (C) 2015 Elsevier B.V. All rights reserved.