APPLIED SURFACE SCIENCE
卷 355, 期 -, 页码 98-103出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.apsusc.2015.07.058
关键词
Microwave synthesis; Zinc oxide; Polarity; Nanoplates; Oxygen defects; Photocatalysis
Photoactive zinc based nanoplates were developed through a rapid microwave synthesis. A low temperature thermolysis reaction in a surfactant medium was initially performed for producing microwave active zinc based polar precursors. Using these precursors, the zinc oxide nanopowder having platelet morphologies were prepared. The nanoplatelets exhibited random growth with non-polar (1 0 1) surface as the major growth plane. The structural and functional features of the resultant zinc oxide samples were monitored using XRD, FTIR, TEM and PL. The photocatalytic activities of the samples were investigated through the standard photoreduction kinetics using the methylene blue dye. The catalytic efficiencies of the samples were checked both under UV and sunlight. A comparative study was also performed with the standard TiO2 sample. The analyses revealed that the microwave derived zinc oxide have higher catalytic efficiency, than the standard titania samples, both under UV and sunlight illuminations. The unique nature of the zinc oxide non-polar surfaces can be attributed due to the presence of more active two dimensional open surfaces and the higher content of oxygen defect concentrations. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据