期刊
RADIATION PHYSICS AND CHEMISTRY
卷 115, 期 -, 页码 62-67出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.radphyschem.2015.05.041
关键词
Radiolytic reduction; PVA stabilized; Silver nanoparticles; Screen printing; Antimicrobial fabrics
资金
- Sarvottam Industries, Jodhpur
Highly stable colloidal solution of silver nanoparticles in a water-isopropanol-polyvinyl alcohol system was prepared through Co-60-gamma radiation at total dose of 35 kGy at dose rate of 5.67 kGy/h under nitrogen atmosphere. Ultraviolet-visible (UV-vis), X-ray diffraction (XRD), Atomic Force Microscopy (AFM) and Scanning Electron Microscopy (SEM) of the obtained colloidal solution indicated the formation of spherical shaped well mono dispersed silver nanoparticles with average diameter about 30 nm having very narrow size distribution. The radiolytically obtained nanosilver colloid was coated onto cotton fabrics by a simple industrial screen printing method and its adhesion with the fabric was found out by leaching studies using Atomic Absorption Spectrophotometry (AAS). Good adhesion was achieved by the adopted method wherein 89.5% of the coated nanosilver was retained in the fabric even after keeping the fabrics soaked in water for more than 60 h. Antimicrobial efficacy tests of the nanosilver coated cotton fabric showed that nanosilver coating is effective in killing both bacterial and fungal strains even at very low nanosilver loading (21.81 mu gm/cm(2)). Nanosilver coating on the cotton fabric did not allow microbes (Pseudomonas aeruginosa, Staphylococcus aureus, Escherichia coli and Candida albicans) to adhere and proliferate on fabric surface. Staphylococci (Staphylococcus aureus) and Yeast (Candida albicans) showed inhibition zones in presence of these nanosilver coated fabrics while no inhibition zone was observed with the uncoated control fabric. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据