Antistatic polymers are required to dissipate static charges safely from component surfaces. Our overall objective has been to develop cost-effective flame-retarded and antistatic polyethylene compounds suitable for rotomolding. This communication considers the surface resistivity and mechanical properties of rotationally molded linear low-density polyethylene (LLDPE)/graphite composites containing natural Zimbabwean graphite, expandable graphite, or expanded graphite. Dry blending and melt compounding were employed to obtain antistatic composites at the lowest graphite contents. Dry blending was found to be an effective mixing method for rotomolding antistatic LLDPE/graphite composites, thereby eliminating an expensive compounding step. Dry-blended Zimbabwean graphite composites showed the lowest surface resistivity at all graphite contents, with a surface resistivity of 10(5) /square at 10 wt% loading. Although rotomolded powders obtained following the melt compounding of Zimbabwean graphite exhibited higher resistivity values, the variability was much lower. Injection molding resulted in surface resistivity values above 10(14) /square for all compositions used. The rotomolded composites exhibited poor mechanical properties, in contrast to injection-molded composites. The Halpin-Tsai model showed good fits to the tensile modulus data for injection-molded Zimbabwean and expandable graphite. (c) 2013 Society of Plastics Engineers
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据