Pure titanium; electroless Ni-B coating; heat treatment; wear; hardness
资金
- Ataturk University [2012/128]
In the present study, the surface of commercial pure (Grade 2) titanium was coated with electroless Ni-B and, then, it was subjected to heat treatment for an hour at 400?. The surface morphology, microstructure and phase identification were analysed by X-ray diffraction and scanning electron microscope. Wear behaviour characterisation was carried out using a ball-on-disc tribometer. The results of the analyses showed that the electroless Ni-B coating had a significantly amorphous structure in the as-deposited condition. It was also determined that the coating structure crystallised after the heat treatment and wear resistance of pure titanium increased after electroless Ni-B coating. Particularly, upon the heat treatment, it was observed that wear resistance and surface hardness of pure titanium considerably increased.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据