JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS
卷 29, 期 4, 页码 519-537出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0892705713519811
关键词
Delamination; glass/epoxy composites; acoustic emission; sentry function
资金
- EPSRC [EP/I02946X/1] Funding Source: UKRI
- Engineering and Physical Sciences Research Council [EP/I02946X/1] Funding Source: researchfish
Among the failure modes of composite materials, delamination is the most striking one. It may result in the reduction of stiffness and long-term performance of composite materials. The initiation stage is very crucial in delamination. This is because initiation stage requires higher amount of force, and after this stage, there is a stable propagation of delamination that requires little force and causes the failure of the structure. Initiation of delamination consists of two main stages including minor initiation and major initiation. These two stages are vital stages in the delamination process. Understanding the delamination behavior and their internal micro events in these stages may lead to better design and result in enhanced strength against crack initiation. This article proposes a combined method to discriminate various fracture mechanisms in the initiation of delamination. The combination of sentry function analysis and frequency analysis of acoustic emission (AE) waveforms are used to analyze crack initiation and to discriminate its internal micro failures during mode I delamination. Discrimination process is derived from the power spectrum density of AE waveform in distinct frequency intervals. Scanning electron microscopy (SEM) observation was used to determine different fracture mechanisms and associate these observed fracture mechanisms and their equivalent AE signal frequency range. It is shown that this combined method is a powerful device to study the behavior of the initiation of delamination.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据