JOURNAL OF THERMAL SPRAY TECHNOLOGY
卷 20, 期 4, 页码 892-897出版社
SPRINGER
DOI: 10.1007/s11666-011-9635-z
关键词
electrical properties; SiC-MoSi2 composite coating; vacuum cold spray oxidation
资金
- National Natural Science Foundation of China [50705075]
SiC-MoSi2 composite powders was prepared by wet milling with MoSi2 powders and SiC loose grinding ball in alcohol solution. Vacuum cold spray (VCS) process was used to deposit SiC-MoSi2 electric conducting composite coatings. The microstructure of the VCS SiC-MoSi2 composite coatings were characterized by scanning electron microscopy. The electrical resistance of the coatings was measured using a four-point probe method. The effects of the deposition parameters on the electrical resistivity of the composite coatings were investigated. The electrical properties of the coatings at elevated temperatures in air and Ar gas atmospheres were also explored. The results show that the electrical resistivity of SiC-MoSi2 coatings decreases with increasing He gas flow rates ranged from 3 to 6 L/min. The electrical resistivity increases with the increase in heat treatment temperature due to pesting behavior of MoSi2. The electric conductive property of the VCS SiC-MoSi2 coating is significantly improved after heat treatment at 1000 A degrees C for 3 h in Ar protective atmosphere without oxidation. A minimum resistivity of the heat treated coating is 0.16 Omega center dot A cm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据