JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 110, 期 3, 页码 1143-1151出版社
SPRINGER
DOI: 10.1007/s10973-011-2027-2
关键词
Nanoparticles; Ferrites; Chemical synthesis; Non-isothermal kinetics; Thermal process
资金
- National Nature Science Foundation of China [21161002]
- Guangxi Nature Science Foundation of China [2011GXNSFA018036]
Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O was synthesized by solid-state reaction at low heat using ZnSO4 center dot 7H(2)O, NiSO4 center dot 6H(2)O, FeSO4 center dot 7H(2)O, and Na2C2O4 as raw materials. The spinel Zn0.5Ni0.5Fe2O4 was obtained via calcining Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O above 773 K in air. The Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O and its calcined products were characterized by thermogravimetry and differential scanning calorimetry (TG/DSC), Fourier transform FT-IR, X-ray powder diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectrometer (EDS), and vibrating sample magnetometer (VSM). The result showed that Zn0.5Ni0.5Fe2O4 obtained at 1073 K had a saturation magnetization of 86.7 emu g(-1). The thermal process of Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O experienced three steps, which involved the dehydration of the six crystal water molecules at first, and then decomposition of Zn0.5Ni0.5Fe2(C2O4)(3) into Zn0.5Ni0.5Fe2O4 in air, and at last crystallization of Zn0.5Ni0.5Fe2O4. Based on KAS equation, and OFW equation, the values of the activation energies associated with the thermal process of Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O were determined to be 126.02 +/- A 23.93, and 259.76 +/- A 18.67 kJ mol(-1) for the first, and second thermal process steps, respectively. Dehydration of the six waters of Zn0.5Ni0.5Fe2(C2O4)(3)center dot 6H(2)O is multi-step reaction mechanisms. Decomposition of Zn0.5Ni0.5Fe2(C2O4)(3) into Zn0.5Ni0.5Fe2O4 could be simple reaction mechanism, probable mechanism function integral form of thermal decomposition of Zn0.5Ni0.5Fe2(C2O4)(3) is determined to be g(alpha) = [-ln(1 - alpha)](4).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据