We developed a persistent phosphor of Y3Al2Ga3O12 doped with Nd3+, Ce3+, Cr3+ ions (YAGG:Nd-Ce-Cr) exhibiting long (>10 h) persistent luminescence at multi-wavelengths of around 880, 1064, and 1335 nm due to f-f transitions of Nd3+ and at 505 nm due to Ce3+:5d(1)-> 4f transition. The intense near-infrared (NIR) persistent luminescence bands from Nd3+ match well with the first (650-950 nm) and second (1000-1400 nm) bio-imaging windows. The NIR persistent radiance of the YAGG: Nd-Ce-Cr phosphor (0.33 x 10(-1) mW/Sr/m(2)) at 60 min after ceasing blue light illumination was over 2 times higher than that of the widely used ZnGa2O4:Cr3+ red persistent phosphor (0.15 x 10(-1) mW/Sr/m(2)). (C) 2015 AIP Publishing LLC.