Effects of a zirconate coupling agent incorporated into an experimental resin composite on its compressive strength and bonding to zirconia

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmbbm.2013.09.007

关键词

Shear bond strength; Zirconia; Coupling agent; Resin composite; Adhesion

向作者/读者索取更多资源

Aim: To assess in vitro the compressive strength of an experimental zirconate coupling agented resin composite and its bonding to dental zirconia ceramics. Methods: Various ratios (1.5-4.0 wt%) of a zirconate coupling agent, NZ-33 (R), zirconium(IV)-2,2[(bis-2-propenolatomethyl)butanolato-tris-2-methyl-2-propenoato-O)] were incorporated in an experimental bis-GMA/MMA-based resin composite formulation with silica fillers. Compressive strength of the experimental resin composite and shear bond strength (SBS) of the resin composite to zirconia were evaluated by using a universal testing machine. Specimens were stored in dry condition, in water storage for 7 days and for 14 days, to a total of twenty test groups. The data were analyzed by one-way ANOVA and Tukey post hoc test (alpha = 0.05). Results: SBS of resin-to-zirconia bonding and compressive strength both have significant increase at 1.5 wt% and 3.0 wt% NZ-33 (R) (p < 0.05). However, water storage for 7 days (p > 0.05) and 14 days (p > 0.05) significantly decreased SBS of the experimental resin-to-zirconia with no significant difference between groups (p > 0.05). Conclusions: An addition of a zirconate coupling agent used might strengthen the biomechanical properties of the experimental resin composite. (C) 2013 Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据