期刊
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
卷 20, 期 -, 页码 227-236出版社
ELSEVIER
DOI: 10.1016/j.jmbbm.2012.11.006
关键词
Stents; Restenosis; Fatigue; Corrosion; Fracture
资金
- European Regional Development Fund
- Republic of Cyprus through the Research Promotion Foundation [PiENEK/0609/78]
Preliminary studies have revealed that some stents undergo corrosion and fatigue-induced fracture in vivo, with significant release of metallic ions into surrounding tissues. A direct link between corrosion and in-stent restenosis has not been clearly established; nonetheless in vitro studies have shown that relatively high concentrations of heavy metal ions can stimulate both inflammatory and fibrotic reactions, which are the main steps in the process of restenosis. To isolate the mechanical effects from the local biochemical effects, accelerated biomechanical testing was performed on single and overlapping Nickel-Titanium (NiTi) stents subjected to various degrees of curvature. Post testing, stents were evaluated using Scanning Electron Microscopy (SEM) to identify the type of surface alterations. Fretting wear was observed in overlapping cases, in both straight and curved configurations. Stent strut fractures occurred in the presence of geometric curvature. Fretting wear and fatigue fractures observed on stents following mechanical simulation were similar to those from previously reported human stent explants. It has been shown that biomechanical factors such as arterial curvature combined with stent overlapping enhance the incidence and degree of wear and fatigue fracture when compared to single stents in a straight tube configuration. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据