Microstructure and mechanical behavior of superelastic Ti-24Nb-0.50 and Ti-24Nb-0.5N biomedical alloys

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/j.jmbbm.2012.01.017

关键词

Titanium alloys; Superelasticity; Stress induced martensite; Deformation twinning

资金

  1. French National Research Agency [ANR 08MAPR 0017]

向作者/读者索取更多资源

In this study, the microstructure and the mechanical properties of two new biocompatible superelastic alloys, Ti-24Nb-0.50 and Ti-24Nb-0.5N (at.%), were investigated. Special attention was focused on the role of O and N addition on alpha '' formation, supereleastic recovery and mechanical strength by comparison with the Ti-24Nb and Ti-26Nb (at.%) alloy compositions taken as references. Microstructures were characterized by optical microscopy, X-ray diffraction and transmission electron microscopy before and after deformation. The mechanical properties and the superelastic behavior were evaluated by conventional and cyclic tensile tests. High tensile strength, low Young's modulus, rather high superelastic recovery and excellent ductility were observed for both superelastic Ti-24Nb-0.50 and Ti-24Nb-0.5N alloys. Deformation twinning was shown to accommodate the plastic deformation in these alloys and only the {332}< 113 > twinning system was observed to be activated by electron backscattered diffraction analyses. (C) 2012 Elsevier Ltd. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据