TFT; Transparent; Oxide; Passivation
资金
- MKE/IITA [2006-S079-02]
We have studied transparent bottom-gate TFTs (thin film transistors) using amorphous IGZO (In-Ga-Zn-O) as an active channel material. The TFT devices had inverse co-planar structures. Source/drain and gate electrodes were constituted by ITO sputtered with a DC-RF magnetron sputter system, and an alkaline-free glass was used as a substrate. The gate insulator was Al(2)O(3) formed by using an atomic layer deposition (ALD) method at 150 degrees C. An active layer was formed by off-axis RF magnetron sputtering and post-annealing was performed with a hot plate or a vacuum oven. The field effect mobilities and the sub-threshold swings of the IGZO TFTS were 12 similar to 18 cm(2)/Vs and 0.2 similar to 0.6 V/dec, respectively. However, the hysteresis on I-V characteristics was relatively large without passivation. Thus. we passivated the TFT devices with inorganic and organic materials. After the organic passivation and post-heat treatments, the hysteresis was remarkably reduced Without deterioration of the electrical characteristics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据