POLYMER DEGRADATION AND STABILITY
卷 115, 期 -, 页码 32-37出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2015.02.013
关键词
Nitrile rubber (NBR); Thermo-oxidative aging; Stress relaxation; Rebound
Continuous stress relaxation of nitrile rubber (NBR) was characterized in air and N-2 at high temperatures (125 degrees C and 165 degrees C). Stress increase (rebound) after decay was observed in air, but not in N-2. Chemical structure, crosslinking density and hardness investigations were carried out to gain insights into the underlying mechanism that governs such behavior. Results indicate that at later stage thermo-oxidative crosslinking prevailed over chain scission causing stress rebound. The effect of atmosphere, temperature and original strain on the stress relaxation is also discussed. (C) 2015 Elsevier Ltd. All rights reserved.