关键词
SiC; Sliding wear; Microstructure; Pressureless sintering; Contact-mechanical properties
资金
- Ministerio de Ciencia y Tecnologia (Government of Spain) [MAT 2010-16848]
- Junta de Extremadura [PRE09041]
The sliding wear of pressureless liquid-phase-sintered (PLPS) SiC ceramics under diesel fuel lubrication was investigated. It was found that the sliding-wear behaviour under diesel fuel is similar to what is observed under lubrication with the chemically similar paraffin oil: initial mild, plasticity-controlled wear followed by severe, fracture-controlled wear, with a well-defined wear transition. Compared to paraffin oil, however, diesel fuel lubrication decreases the extent of the mild-wear regime and results in damage that is more severe due to its lower viscosity. Also, it was found that the wear resistance under diesel fuel decreases with increasing contact load and sliding speed. Subsequent investigation of the effects of the intergranular phase content, grain size, and grain shape demonstrates nevertheless that the wear performance of PLPS SiC under diesel lubrication can be improved via rnicrostructural control by (i) decreasing the intergranular phase content, and (ii) decreasing the SiC grain size or increasing its aspect ratio. The results of this work are likely to have relevant implications for the design of wear resistant PLPS SiC ceramic components for diesel engines. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据