The microwave dielectric properties of the (1 - x)Li2TiO3-xZnO(x = 0.1-0.5) ceramic system prepared by mixed oxide route have been investigated. The rock-salt structured (1 - x)Li2TiO3-xZnO were characterized by using X-ray diffraction spectra, scanning electron microcopy (SEM). The dielectric properties are strongly dependent on the compositions, the densifications and the microstructures of the specimens. The decrease of Q x f value at high-level ZnO addition (x > 0.3) was owing to the intensity of the (0 0 2) superstructure reflection decreased and became disordered rock-salt structure. For practical applications, a new microwave dielectric material 0.7Li(2)TiO(3)-0.3ZnO is suggested and it possesses a good combination of dielectric properties with an epsilon(r) of similar to 22.95, a Q x f of similar to 99,800 GHz (measured at 8.91 GHz), and a tau(f) of similar to 0 ppm/degrees C. A low-loss dielectric resonant antenna using aperture-coupled cylindrical dielectric resonant was designed and fabricated using the proposed dielectric to study its performance. (c) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据