JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 32, 期 8, 页码 1759-1767出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2012.01.007
关键词
Shaping; Nanocomposites; Strength; Carbon; Wear parts
资金
- Innovation Promotion Agency CTI of Switzerland [CTI 9611.1 PFNM-NM]
The utilization of silicon-based polymers as a source of amorphous non-oxide ceramics obtained upon pyrolytic treatment of them is increasingly gaining attention in research and is currently expanding into the field of commercial products. This work is focused on the near-net shaped fabrication, mechanical and tribological properties of a polymer-derived Si/C/N system. Small sub-millimetre thick ceramic test discs and bars were fabricated by casting of polysilazane and/or polycarbosilane precursor mixtures into elastomeric polydimethylsiloxane forms, thermal cross-linking and subsequent pyrolysis. Additional carbon was introduced on the molecular level using triphenylvinylsilane as the precursor, its cross-linking with the polymers via hydrosilylation prohibits phase separation of graphite within. the amorphous matrix. The characteristic strength of nearly 700 MPa along with stable low friction coefficients in sliding against similar polymer-derived ceramics testifies to their potential in micro electro mechanical system applications. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据