JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 32, 期 1, 页码 97-105出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2011.07.032
关键词
TaB2; Microstructure; Mechanical properties; Oxidation resistance; Nanoindentation
TaB2-based ceramics were hot pressed in low vacuum with addition of 5-10 vol% MoSi2. Temperatures in the range of 1680-1780 degrees C led to relative density around 90-95%. The hardness was about 18 GPa, the fracture toughness 4.6 MPa m(1/2) and the room temperature flexural strength was around 630 MPa, but abruptly decreased above 1200 degrees C to 220 MPa. The composite containing 10 vol% of MoSi2 was tested in a bottom-up furnace in the temperature range 1200-1700 degrees C for 30 min. The microstructure appeared covered by a SiO2 layer, whose thickness increased with the temperature, but the bulk remained unaltered up to 1600 degrees C. At 1700 degrees C the specimen vaporized. Nanoindentation was employed on the oxidized cross sections in order to detect eventual mechanical properties modification associated to chemical/microstructural change, like formation of Ta-B-O solid solutions. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据