期刊
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 32, 期 14, 页码 3733-3743出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2012.04.038
关键词
BSCF; Barium strontium cobalt iron oxide; Second phase; Grain growth; Kinetic demixing/decomposition
资金
- U.S. Air Force Office of Scientific Research (AFOSR) [FA9550-10-1-0185]
Microstructural changes due to kinetic demixing within sintered BSCF ceramics (Ba0.5Sr0.5CoxFe1-xO3-delta, x = 0.2 and 0.8: BSCF5528 and BSCF5582, respectively) have been investigated. When the specimens were subjected to 2 A/cm(2) at 1000 degrees C and pO(2) = 10(-5) atm, there was a significant enhancement of grain growth as well as 2nd phase formation observed in BSCF5528. At the anode, cobalt deficient aggregates within the grains; and, at the cathode, cobalt rich 2nd phase particles were observed on the grain surfaces of the microstructure. Such phenomena were not observed in BSCF5582, even under higher current density (7 A/km(2)) and longer delay time. These results were explained by the kinetic demixing/decomposition. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据