期刊
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 32, 期 4, 页码 727-736出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2011.10.005
关键词
MgO; MgAl2O4; Zircon; Composite; Refractory; Corrosion
资金
- Anadolu University
- TUBITAK [106M394]
- Konya Selcuklu Krom Magnezit Tugla Sanayi A.S.
Corrosion behaviours of MgO-spinel-ZrSiO4 compositions were investigated. The influence of corrosion resistance based on the microstructural changes occurred due to the solubilities of constituents in corroded regions was examined using SEM/EDX analysis. The following observations were determined by microstructural characterisation performed at the interface of clinker refractory: (i) the formation of ZrO2 and Mg2SiO4 phases among MgO grains after sintering, (ii) the formation of CaZrO3 phase during penetration, (iii) prevention of penetration by new phases formed making a barrier effect against clinker with an improvement in densification, and (iv) the decrease in the amount of CaO and the increase in the quantity of MgO using EDX analysis made moving from clinker towards refractory. The addition of ZrSiO4 reduced the values of penetration and spreading areas of the corroded regions of composite refractories and improved the corrosion resistance significantly, leading to a long service life of MgO spinel zircon based refractories for industrial applications. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据