JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 31, 期 10, 页码 1889-1895出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2011.04.003
关键词
Ceramic matrix composites; Alumina; YAG
资金
- Polish Ministry of Science and High Education [NN 507 457737]
The preparation technique of the particulate composite materials in the alumina/YAG system was elaborated. Within alumina particles suspension yttria precursor was precipitated with ammonium carbonate. Drying and calcination at 600 degrees C resulted in the mixture of alumina and yttria particles, the latter being much finer than alumina particles. This mixture was additionally homogenized by short attrition milling in an aqueous suspension. Sintering of such powders results in the materials composed of YAG inclusions of sizes smaller than shown by alumina grains and evenly distributed within the matrix. YAG particles result from the reaction of Y2O3 with Al2O3 during heat treatment. YAG inclusions limit effectively grain growth of the alumina matrix. Hardness, fracture toughness, strength, Young modulus and wear susceptibility of composites and pure alumina were measured. Composites show higher hardness and in some cases higher fracture toughness and wear resistance than pure alumina polycrystals. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据