JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 29, 期 1, 页码 39-46出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2008.05.026
关键词
B. Microstructure-final; B. Electron microscopy; D. Glass ceramics; B. Mullite; Cordierite
The effect Of V2O5 nucleant on crystallization of stoichiometric cordierite glass ceramics in the presence of various amounts of BaO and Al2O3 additives were investigated by DTA, XRD and SEM. It was shown that 3 wt.% V2O5 and 1.5 wt.% BaO were the optimum amounts of the additives effective in inducing both surface and bulk crystallization in the above glass ceramics. This resulted in similar to 90 wt.% cordierite after a 3 h heat treatment at 1020 degrees C. The specimens possessing 4-5 wt.% Al2O3 in excess of the stoichiometric cordierite composition, developed mullite along with cordierite in the temperature range of 1045-1055 degrees C, whereas in the specimen containing 6 wt.% excess Al2O3, mullite was detected as the sole crystallization product. (c) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据