期刊
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 28, 期 2, 页码 431-435出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2007.03.006
关键词
surfaces; corrosion; mullite; structural application
In the development of environmental barrier coating system for silicon nitride ceramic, a corrosion behavior of mullite was examined under static state water vapor environment at elevated temperatures. Results showed that a small amount of sodium, which was present in mullite bulk as an impurity, accelerated the water vapor corrosion of silica component and decomposition of mullite into alumina phase. To improve the selective corrosion of the boundary phase in silicate compounds, a mullite/Lu2Si2O7 eutectic system without boundary glassy phase was developed. The eutectic composition was Al2O3:SiO2:Lu2O3 = 27.3:54.6:18.1 in molar ratio and the eutectic temperature was estimated to be similar to 1500-1520 degrees C. No weight loss was measured after the static state water vapor corrosion test at 1300 degrees C for 100 h. However, the recession of mullite phase in the eutectic oxide occurred after exposure to high speed steam jet environment at 1200 degrees C. (c) 2007 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据