期刊
JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 159, 期 8, 页码 A1318-A1322出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.082208jes
关键词
-
资金
- German Science Foundation DFG [PAK-177]
- German Ministry of Education and Research (BMBF) [LIB 2015]
The clathrate-II compound NaxSi136 (x -> 0) was synthesized as a precursor for electrochemical lithiation via sodium extraction from the Zintl-Phase NaSi. The final composition was determined to be Na1.3Si136 via a Rietveld refinement. Electrochemical lithiation of this clathrate-II compound yielded a potential plateau at 300 mV whose capacity is in good agreement with 24 lithium atoms being inserted in the clathrate-II structure. In order to prove this assumption, several clathrate-containing electrodes were prepared and electrochemically lithiated. Afterwards the electrode material was investigated using Li-7 magic-angle spinning (MAS)-NMR spectroscopy. Two signals in a 2:1 ratio at extremely high chemical shifts of 412 and 433 ppm, respectively, relative to 1M aqueous lithium chloride solution, were detected and give the indisputable evidence that lithiation of the clathrate-II framework was successful. Hence, this work presents a new method for filling clathrate cages and moreover, the first lithium containing clathrate compound. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.082208jes] All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据