JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 158, 期 4, 页码 A396-A399出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/1.3551533
关键词
-
资金
- US Department of Energy's Argonne National Laboratory
LiZr2-xTix(PO4)(3) with x 0, 0.5, and 1.0 were synthesized by a sol-gel method and electrochemically cycled as an anode for Li-ion batteries. LiZr2-xTix(PO4)(3) with rhombohedral structure (space group, R (3) over barc) underwent irreversible amorphization during the first Li insertion, leading to a large loss of the discharge capacity. The resulting amorphous phase, however, well maintained their discharge capacity (60.4 mAh g(-1), 74.6 mAh g(-1), and 149.6 mAh g(-1) for LiZr2(PO4)(3), LiZr1.5Ti0.5(PO4)(3), and LiZrTi(PO4)(3), respectively, cycled 0.2 mA cm(-2) between 0.1 and 3 V) during an extended electrochemical cycling. It was shown that the Ti addition substantially increased the discharge capacity of LiZr2(PO4)(3), although the addition caused gradual capacity fading during cycling when added in excess. (C) 2011 The Electrochemical Society. [DOI: 10.1149/1.3551533]
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据