期刊
JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 157, 期 5, 页码 A582-A588出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/1.3332806
关键词
nanoparticles; NMR spectroscopy; secondary cells; titanium compounds; X-ray absorption spectra
资金
- HASYLAB
- Netherlands Organization for Scientific Research (NWO)
Amorphous titanium oxide nanoparticles were prepared from titanium isopropoxide. In situ measurements reveal an extraordinary high capacity of 810 mAh/g on the first discharge. Upon cycling at a charge/discharge rate of 33.5 mA/g, this capacity gradually decreases to 200 mAh/g after 50 cycles. The origin of this fading was investigated using X-ray absorption spectroscopy and solid-state nuclear magnetic resonance. These measurements reveal that a large fraction of the total amount of the consumed Li atoms is due to the reaction of H2O/OH species adsorbed at the surface to Li2O, explaining the irreversible capacity loss. The reversible capacity of the bulk, leading to the Li0.5TiO2 composition, does not explain the relatively large reversible capacity, implying that part of Li2O at the TiO2 surface may be reversible. The high reversible capacity, also at large (dis)charge rates up to 3.35 A/g (10C), makes this amorphous titanium oxide material suitable as a low cost electrode material in a high power battery.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据