JOURNAL OF THE BRAZILIAN CHEMICAL SOCIETY
卷 19, 期 4, 页码 788-794出版社
SOC BRASILEIRA QUIMICA
DOI: 10.1590/S0103-50532008000400025
关键词
vanadium oxide film; chronopotentiometric; DC measurements
Amorphous vanadium oxide films were synthesized onto ITO-coated glass substrates by the hot filament metal oxide deposition technique. The as-deposited samples were heat-treated in an argon atmosphere. X-ray diffraction analysis revealed that the films treated at 200 and 300 degrees C were still amorphous, while those treated at 400 and 500 degrees C were crystalline, with a V2O5 structure. All electrodes were electrochemically reversible for Li+ intercalation, exhibiting the electrochromic effect, observed from optical transmittance measurements at 632.8 nm. The Li-diffusion coefficient, DC, was measured by the galvanostatic intermittent titration technique (GITT) as function of the inserted charge. For the crystalline films it was observed that the optical absorbance and the DC increase with increasing Li insertion in the single-phase regions of crystalline LixV2O5 and decrease in the two-phase regions. For the latter, an effective DC was considered. The presence of other vanadium oxides mixed to the V2O5 matrix was inferred for the crystalline films from the chronopotentiometric and DC measurements.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据