期刊
JOURNAL OF SUPERCRITICAL FLUIDS
卷 94, 期 -, 页码 165-173出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.supflu.2014.07.011
关键词
Titanate nanotube; Supercritical hydrothermal treatment; Titanate hierarchical sphere; Titanate nanosheet; Anatase nanorod
资金
- National Natural Science Foundation of China [51176113]
A novel template- and organic-free synthesis of TiO2 nanostructures with controlled phase and morphology was realized through batch supercritical hydrothermal treatment (400 degrees C) of titanate nanotubes (TNTs) with H2O2 in NaOH aqueous solution. Well-defined 3D titanate hierarchical spheres (THSs), 2D multilayered titanate nanosheets (TNSs), and 1D monodisperse anatase nanorods (ANRs) exposing (0 1 0) facets were prepared in 15 min by slightly varying the NaOH solution pH. Specifically, the obtained Na/H-THSs (without/with HCl neutralization) exhibited highly porous structures with large specific surface area (109 m(2) g(-1) and 196 m(2) g(-1), respectively). Temperature-dependent phase and morphology evolutions of products under subcritical condition (200 and 300 degrees C) were investigated. The formation of the TiO2 nanostructures from TNTs was proposed mainly following a dissolution-nucleation-growth mechanism, suggesting that both supercritical temperature and NaOH solution pH were determinant factors governing the nucleation and growth process and thus the phase and morphology. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据