期刊
JOURNAL OF SUPERCRITICAL FLUIDS
卷 57, 期 1, 页码 87-94出版社
ELSEVIER
DOI: 10.1016/j.supflu.2011.01.011
关键词
Microcellular foaming; Amorphous polymers; Additives; Supercritical carbon dioxide; Nanostructured
资金
- ANR (Agence Nationale de la Recherche)
Microcellular foaming of amorphous rigid polymers, polymethylmethacrylate (PMMA) and polystyrene (PS) was studied in supercritical CO2 (ScCO2) in the presence of several types of additives, such as triblock ( styrene-co-butadiene-co-methylmethactylate, SBM and methylmethacrylate-co-butylacrylate-co-methylmethacrylate, MAM) terpolymers. This work is focused in the two-step foaming process, in which the sample is previously saturated under ScCO2 being expanded in a second step out of the CO2 vessel (e.g. in a hot oil bath) where foaming is initiated by the change of temperature near or above the glass transition temperature of the glass/polymer glassy system. Samples were saturated under high pressures of CO2 (300 bar), at room temperature, for 16 h, followed by a quenching at a high depressurization rate (150 bar/min). In the last step, foaming was carried out at different temperatures (from 80 degrees C to 140 degrees C) and different foaming times (from 10 s to 120s). It was found that cellular structures were controlled selecting either the additive type or the foaming conditions. Cell sizes are ranging from 0.3 mu m to 300 mu m, and densities from 0.50 g/cm(3) to 1 g/cm(3) depending on the polymers considered. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据