期刊
JOURNAL OF SOLID STATE ELECTROCHEMISTRY
卷 16, 期 5, 页码 1999-2004出版社
SPRINGER
DOI: 10.1007/s10008-011-1602-6
关键词
SnS2; Graphene; Solvothermal synthesis; Lithium-ion battery
资金
- China Postdoctoral Science Foundation [20100471296]
- Postdoctoral Foundation of Jiangsu Province [1001003C]
- National Nature Science Foundation of China [60928009, 61076017, 60990314]
Graphene-SnS2 nanocomposites were prepared via a solvothermal method with different loading of SnS2. The nanostructure and morphology of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The XRD patterns revealed that hexagonal SnS2 was obtained. SEM and TEM results indicated that SnS2 particles distributed homogeneously on graphene sheets. The electrochemical properties of the samples as active anode materials for lithium-ion batteries were examined by constant current charge-discharge cycling. The composite with weight ratio between graphene and SnS2 of 1:4 had the highest rate capability among all the samples and its reversible capacity after 50 cycles was 351 mAh/g, which was much higher than that of the pure SnS2 (23 mAh/g). With graphene as conductive matrix, homogeneous distribution of SnS2 nanoparticles can be ensured and volume changes of the nanoparticles during the charge and discharge processes can be accomodated effectively, which results in good electrochemical performance of the composites.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据