PVA nanocomposites reinforced with Zn2Al LDHs, intercalated with orange dyes

Zn2Al-layered double hydroxides (LDH) were intercalated with anions of the dyes Orange G, Orange II, and Methyl Orange by alkaline co-precipitation of aqueous solutions of zinc chloride and aluminum nitrate simultaneously in the presence of dye sodium salts. Transparent, homogeneous, and colored nanocomposite films were obtained by casting after dispersing the dye-intercalated LDHs (pigments) into commercial poly(vinyl alcohol) (PVA). The films were characterized by X-ray diffraction, ultraviolet-visible spectroscopy, thermal analysis (thermogravimetric analysis (TGA)) and differential thermal analysis (DTA)), and mechanical testing. Mechanical reinforcement of the PVA compounded with the dye-intercalated LDHs was achieved, and reasonable increases in Young's modulus and ultimate tensile strength were observed with as little as 0.5% added filler, while larger amounts tended to decrease the reinforcement effect. These results demonstrate the onset of a new range of potential applications for layered double hydroxide intercalated with dyes in the preparation of polymer composite multifunctional materials.