JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
卷 56, 期 2, 页码 107-113出版社
SPRINGER
DOI: 10.1007/s10971-010-2282-x
关键词
Aerogel; Silica; Rayleigh scattering; Transparency; Methyltrimethoxysilane; Supercritical drying
资金
- New Energy and Industrial Technology Development Organization (NEDO), Japan
Silica-based aerogels with high transparency and high bending strength were prepared using methyltrimethoxysilane and non-ionic surfactant under supercritical drying condition of CO2. Non-ionic surfactant, ethylene oxide/propylene oxide block copolymer, was appropriate to form the three dimensional-connected thinner fibers of silica skeletons, which was extruded by soaking the wet gel in hot water at 50 A degrees C, resulting in the formation of porous materials having small pores with narrow size distribution. The transparency of aerogels increased with decreasing the pore size, reaching to higher than 65 and 88% at 400 and 600 nm wavelength, respectively, for 10 mm thickness of sample. The formation of fiber skeletons were discussed using small angle X-ray scattering experiments.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据