JOURNAL OF REINFORCED PLASTICS AND COMPOSITES
卷 32, 期 9, 页码 612-618出版社
SAGE PUBLICATIONS LTD
DOI: 10.1177/0731684413481862
关键词
Liquid epoxidized natural rubber; glass fiber; epoxy; weight percentage; mechanical properties
资金
- Universiti Kebangsaan Malaysia
- Ministry Of Higher Education
Glass fiber epoxy composites are widely used in industries. Liquid epoxidized natural rubber was added to epoxy as the matrix for a fiber-reinforced composite in order to improve its mechanical properties whilst E-glass fiber was used as the composite reinforcement. Flexural test, Izod impact test, tensile test, thermogravimetric analysis, and scanning electron microscopy were performed to investigate the effect of liquid epoxidized natural rubber addition and glass fiber loadings on the mechanical properties of the composite. It was observed that the flexural strength and flexural modulus of the samples increased with increasing glass fiber percentage with 9% as the maximum weight percentage recorded. The tensile strength and Young's modulus increased with increasing glass fiber content until it reached the maximum value at 9 wt% of glass fiber. The same trend was observed with the impact value of the samples. All the tests were conducted for the composite with and without liquid epoxidized natural rubber addition. The presence of liquid epoxidized natural rubber improved the mechanical properties of the composites due to the plasticizing effect of the rubber particles in the matrix. Thermogravimetric analysis revealed the thermal stability of the composites whilst the scanning electron microscopy shows a heterogeneous dispersed phase of morphology. There was poor adhesion between the matrix polymer and glass fibers due to the use of untreated glass fibers.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据