期刊
JOURNAL OF RARE EARTHS
卷 31, 期 6, 页码 572-576出版社
ELSEVIER
DOI: 10.1016/S1002-0721(12)60322-6
关键词
MnOx-CeO2; NO oxidation; co-precipitation; rare earths
资金
- National High Technology Research and Development Program of China (863 Program) [2011AA03A405]
The NO oxidation reaction was studied over MnOx-CeO2 catalysts prepared by co-precipitation, impregnation and mechanical mixing method, respectively. It was found that the co-precipitation was the most active and a 60% NO conversion was achieved at 250 degrees C. X-ray diffraction (XRD), Brumauer-Emmett (BET), H-2-temperature programmed reduction (H-2-TPR) and oxygen storage capacity (OSC) techniques were employed to characterize the physical and chemical properties of the catalysts. XRD results showed that amorphous MnOx or Mn-O-Ce solid solution existed in co-precipitation and impregnation prepared sample, while crystalline MnOx was found in mechanical mixing catalyst. A larger surface area was observed on co-precipitation prepared catalyst compared to those prepared by impregnation and mechanical mixing. The strong interaction between MnOx and CeO2 enhanced the reducibility of the oxides and increased the amount of Mn4+ and activated oxygen, which are favorable for NO oxidation to NO2.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据