JOURNAL OF RAMAN SPECTROSCOPY
卷 45, 期 5, 页码 383-391出版社
WILEY
DOI: 10.1002/jrs.4472
关键词
TEM; powellite; Mo-rich borosilicate; irradiation-induced damage; raman mapping
类别
The irradiation-induced damages and structure modifications of rare earths doped powellite single crystal have been precisely studied using optical and electron microscopy techniques, including optical interferometry, confocal micro-Raman spectroscopy and transmission electron microscopy. The surface of powellite crystal pops out anisotropically after exposing under Ar ion beam, with a saturation swelling value of 2.0% along a-axis and 1.3% along the c-axis of powellite at high dose. Raman mapping on focused ion-beam sections (5 x 3 mu m(2)) perpendicular to the irradiated surface reveals that irradiation damage induces orientation-dependent compressive stresses in powellite. However, no significant anisotropic effect has been found on the irradiation-induced structural disorder in powellite. At low dose (0.012 dpa), the main irradiation-induced defects created in powellite crystal are small defect clusters. By comparison, the dominant kinds of defects in high-dose (5.0 dpa) sample are dislocations loops and networks. Copyright (c) 2014 John Wiley & Sons, Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据