Pitting on iron; Passive film on iron; in situ Raman Microscopy; Near Resonance Enhancement; Potentiodynamic polarisation
类别
资金
- National Research Foundation [2053306]
- University of the Witwatersrand
- DST/NRF Centre of Excellence in Strong Materials
The composition of the surface film formed on pure iron was investigated in a solution of 0.05?M NaOH and 0.05?M NaCl. Raman spectra of the film were recorded in situ during anodic polarisation over the passive region after addition of the NaCl to the electrolyte, under conditions of preresonance enhancement using excitation at 636.4?nm. Multivariate curve resolution with alternating least squares analysis was applied to the spectra to measure the relative amounts of different iron oxide and oxyhydroxides in the film at different potentials. The water content was also determined in this way from Raman spectra recorded using excitation at 514.5?nm. It was found that the composition of the film and the amount of incorporated water were influenced by the applied anodic potential. The results show that stable pitting can occur when the composition changes from the primary constituents beta-FeOOH and Green Complex (a hydrated, amorphous magnetite) with smaller amounts of ?-Fe2O3 and ?-FeOOH, to d-FeOOH and Green Complex, simultaneously with a reduction in water content. These changes result in conditions that favour the rate of localised breakdown of the film by Cl- ions over the rate of repassivation by water in the passive film. Copyright (c) 2011 John Wiley & Sons, Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据