JOURNAL OF POWER SOURCES
卷 254, 期 -, 页码 249-257出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2013.12.092
关键词
Nanotube arrays; Nickel cobalt sulfide; Supercapacitors; Asymmetric
资金
- National Natural Science Foundation of China [61172003, 51102104, 51302097]
- Wuhan Planning Project of Science and Technology [2013011801010594]
Self-standing NiCO2S4 nanotube arrays have been in situ grown on Ni foam by the anion-exchange reaction and directly used as the electrode for supercapacitors. The NiCO2S4 nanotube in the arrays effectively reduces the inactive material and increases the electroactive surface area because of the ultrathin wall, which is quite competent to achieve high utilization efficiency at high electroactive materials mass loading. The NiCO2S4 nanotube arrays hybrid electrode exhibits an ultrahigh specific capacitance of 14.39 F cm(-2) at 5 mA cm(-2) with excellent rate performance (67.7% retention for current increases 30 times) and cycling stability (92% retention after 5000 cycles) at a high mass loading of 6 mg cm(-2). High areal capacitance (4.68 F cm(-2) at 10 mA cm(-2)), high energy density (31.5 Wh kg(-1) at 156.6 W kg(-1)) and high power density (2348.5 W kg(-1) at 16.6 Wh kg(-1)) can be achieved by assembling asymmetric supercapacitor with reduced graphene oxide at a total active material mass loading as high as 49.5 mg. This work demonstrates that NiCO2S4 nanotube arrays structure is a superior electroactive material for high-performance supercapacitors even at a mass loading of potential application-specific scale. (c) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据