JOURNAL OF POWER SOURCES
卷 263, 期 -, 页码 158-162出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2014.04.038
关键词
Sodium-ion battery; Negative electrode; Pyrolytic carbon from graphite oxide; Intercalation
Carbons with various interlayer spacings of 0.422-0.334 nm were prepared from the pyrolysis of graphite oxide at various temperatures. Raman measurement indicated that these carbons contain many defects even when the interlayer spacing was almost comparable to that of graphite. The charge and discharge potentials monotonically changed when they were used for the negative electrode of sodiumion battery, which was rather similar to that observed for soft carbons. The maximum reversible capacity reached 252 mAh g(-1) for the carbon prepared at 300 degrees C and it showed relatively good cycling stability. The X-ray diffraction pattern of it after charged to 0 V indicated that sodium ions are inserted between the carbon layers, forming a stage 1 intercalation compound. The capacity slightly decreased as the increase in the temperature for pyrolysis and more steeply decreased above 900 degrees C, however, the carbon obtained at 1000 degrees C still delivered a capacity of 95 mAh g(-1). (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据