DOI: 10.1016/j.jpowsour.2014.03.070
关键词
All-solid-state Li ion battery; Solid electrolyte; Garnet structure; Li ion conductivity; Doping
Li2La3Zr2O12 (LLZ) solid electrolytes with Zr site partially substituted by Ta and Nb elements were prepared via the conventional solid-state reaction. All the compositions could lead to the cubic garnet-type structure after sintering at 1150 degrees C. The use of gamma-Al2O3 as a sintering aid in the preparation of doped LLZ was studied. It was shown that Al could help to improve the micro-structure for Nb doping, but not necessary for Ta doping. The Ta and Nb doping enhanced the ionic conductivity at 25 degrees C to 4.09 x 10 (-4) S cm-(1) and 4.50 x 10(-4) S cm(-1), respectively. A conductivity as high as 1.23 x 10(-3) S cm(-1) was obtained when measured at 50 C in air for the Nb-doped LLZ. All-solid-state batteries with LLZTa and LLZNb solid electrolytes were assembled and tested. The cyclic voltammetry (CV) measurement indicated the successful working of the batteries. (c) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据