JOURNAL OF POWER SOURCES
卷 270, 期 -, 页码 106-112出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2014.07.063
关键词
Activated carbon fiber; Energy storage; Lignin; Supercapacitor
资金
- California EISG [12-02TE]
Highly porous submicron activated carbon fibers (ACFs) were robustly generated from low sulfonated alkali lignin and fabricated into supercapacitors for capacitive energy storage. The hydrophilic and high specific surface ACFs exhibited large-size nanographites and good electrical conductivity to demonstrate outstanding electrochemical performance. ACFs from KOH activation, in particular, showed very high 344 F g(-1) specific capacitance at low 1.8 mg cm(-2) mass loading and 10 mV s(-1) scan rate in aqueous electrolytes. Even at relatively high scan rate of 50 mV s(-1) and mass loading of 10 mg cm(-2), a decent specific capacitance of 196 F g(-1) and a remarkable areal capacitance of 0.55 F cm(-2) was obtained, leading to high energy density of 8.1 Wh kg(-1) based on averaged electrodes mass. Furthermore, over 96% capacitance retention rates were achieved after 5000 charge/discharge cycles. Such excellent performance demonstrated great potential of lignin derived carbons for electrical energy storage. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据