JOURNAL OF POWER SOURCES
卷 221, 期 -, 页码 149-156出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2012.07.126
关键词
SOFC; Anode; Barium; LSCM
Three perovskites with the general formula La0.75BaxSr0.25-xCr0.5Mn0.5O3 (x = 0, 010 and 0.25) have been synthesized. For all materials, the symmetry is rhombohedral (space group R-3c). On the electrical point of view, a p-type semiconducting behaviour was evidenced in the series. The addition of barium yields an increase in total conductivity in argon from 18 S cm(-1) for La0.25Sr0.25Cr0.5Mn0.5O3 to 26 S cm(-1) for La0.75Ba0.25Cr0.5Mn0.5O3 at 900 degrees C. However, in H-2-3% H2O, the total conductivity decreases for all compositions and it decreases with barium substitution (0.9 S cm(-1) for La0.75Sr0.25Cr0.5Mn0.5O3 and 0.5 S cm(-1) for La0.75Ba0.25Cr0.5Mn0.5O3 at 900 degrees C). Steady state and impedance spectroscopy measurements were performed on dense pin-shaped electrodes (x = 0 and 0.25) in H-2-3% H2O between 800 and 900 degrees C. For x = 0.25, electrochemical performances are interesting for an applicability as an SOFC anode. Origins of individual contributions to the electrode reaction mechanism are discussed. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据