期刊
JOURNAL OF POWER SOURCES
卷 240, 期 -, 页码 140-148出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2013.04.006
关键词
Lithium nickel cobalt manganese oxide; Aerogel template; Macro porosity; Cathode material; Lithium ion battery
资金
- Key Science and Technology Innovation Team of Zhejiang Province [2010R50013]
- National Science and Technology Support Program [2012BAK30B04]
Macroporous Li1.2Mn0.54Ni0.13Co0.13O2 cathode materials with high crystallinity and hexagonal ordering are synthesized by aerogel template followed by solid state reaction. High discharge capacities of 244.0 mA h g(-1) and 153.9 mA h g(-1) are obtained for the Li-rich layered oxide synthesized at 800 degrees C at current densities of 200 mA g(-1) and 2000 mA g(-1) between 2.0 V and 4.8 V. Increasing the synthesis temperature to 900 degrees C, the macroporous Li1.2Mn0.54Ni0.13Co0.13O2 delivers a high discharge capacity of 220.2 mA h g(-1) at a current density of 200 mA g(-1) with a capacity retention of 89.1% after 50 cycles, 129.8 mA h g(-1) at a current density of 2000 mA g(-1) and almost no capacity fading after 120 cycles. The diffusion coefficients of Li+ in the Li-rich layered oxide determined by galvanostatic intermittent titration technique are in the range of 5.0 x 10(-1)8-8.0 x 10(-14) cm(2) s(-1). Electrochemical impedance spectroscopy indicates that the macroporous structure with good particle contact of the layered oxide can improve its rate capability and cyclic stability. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据