Synthesis of hierarchical mesoporous nest-like Li4Ti5O12 for high-rate lithium ion batteries

期刊

JOURNAL OF POWER SOURCES
卷 200, 期 -, 页码 59-66

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2011.10.052

关键词

Lithium titanate; Hierarchical; Nest-like; Mesoporous; Lithium ion batteries

资金

  1. National Natural Science Foundation of China [21103108, 21173148]
  2. Toyota Motor Corporation
  3. Shanghai Jiao Tong University

向作者/读者索取更多资源

Hierarchical mesoporous nest-like Li4Ti5O12 is prepared by a hydrothermal reaction, using CTAB as the surfactant, and water-soluble titanium complex [NH4+](4)[H+](2)[Ti-4(C2H2O3)(4)(C2H3O3)(2)(O-2)(4)O-2](6-) as the titanium precursor. As-prepared Li4Ti5O12 has a tiny crystallite size of 8.2 nm and a very large surface area of 219.2 m(2) g(-1). Commercial micrometer-sized Li4Ti5O12 is also tested for comparision, and up to 10 000 mA g(-1) (57 C) is applied to evaluate these two samples as the anode material for lithium ion batteries. Our products deliver much better cycling and rate performances, especially at high current densities. 135.1 mAh g(-1) is obtained after 200 cycles at 2500 mA g(-1), and 113.6 mAh g(-1) is obtained at 10 000 mA g(-1). The polarization in our products is much lower, and our products also show higher lithium diffusion coefficient and higher exchange current density, calculated from CV and EIS measurements. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据